(726a) High Flux CO2-Selective Single-Layer Graphene Membranes: Synthesis and Scale-up

Nanoporous single-layer graphene (N-SLG), prepared by incorporating subnanometer vacancy defects in the graphene lattice, is highly promising for high flux gas separation because the resistance to diffuse is controlled by a single transition state at the nanopore [1–3]. Molecular sieving resolution (MSR), defined as the difference in the kinetic diameters of molecules to be separated, of 0.3-0.5 Ã… is needed for CO₂/N₂ and CO₂/CH₄ separation, respectively [4-5].

In this presentation, I will share recent developments in our laboratory on advances on N-SLG membranes including their scale-up to practical dimensions [6-8]. Strategies including controlled etching of graphene lattice, functionalization of graphene lattice as well as hybrid graphene-polymer membranes will be discussed. Specifically, I will discuss a novel etching chemistry, allowing controlled nucleation and expansion of vacancy defects, and yielding MSR of 0.2 Ã…. We show that molecular cutoff can be adjusted by 0.1 Ã… by a slow expansion of nanopores, making O₂/N₂ separation possible from atom-thick membranes. Large CO₂ permeances (above 10000 GPU) combined with attractive CO₂/N₂ separation factor (above 20), makes N-SLG membranes highly promising for postcombustion carbon capture. We show that molecular sieving (selectivities > 20) can be obtained from large graphene coupons reaching 1 cm² in size.

References

• Jiang et al., Nano Lett. 9, 4019–24 (2009).
• Celebi et al,. Science. 344, 289–92 (2014).
• Li et al., Science. 342, 95–98 (2013).
• Yuan et al., ACS Nano. 11, 7974–7987 (2017).
• Koenig et al., Nanotechnol. 7, 728–732 (2012).
• He et al., Energy Environ. Sci. 12, 3305–3312 (2019).
• Zhao et al., Sci. Adv. 5, eaav1851 (2019).
• Huang et al., Nat. Commun. 9, 2632 (2018).