To overcome the disadvantages of TSA, alternative heating methods are investigated. Electrical swing adsorption is one of the options. It also fits in the purpose of electrification of the industrial processes. This alternative way to increase the temperature is believed to be more rapid, more efficient and able to reach higher product concentration than conventional heating methods 1,2,3. These changes could be important for the economic feasibility of CO2 capture. However, to be suitable for ESA, new requirements in terms of adsorbent materials arise as the porous solid phase needs to conduct electricity on top of the demand for good and selective CO2 adsorption.
In this work, 3D-printed honeycomb monoliths, consisting mainly of activated carbon, were produced using Three-Dimensional Fiber Deposition (3DFD). This method results in interwoven structures with easy control on channel size, fiber thickness and geometry of the channels 6,7.
The monolithic structures were investigated in terms of isotherms, porosity, mass transfer limitations and electrical characteristics. Next, they were subjected to consecutive cycles to look at the impact on their adsorption capacity regarding the regeneration method. The regeneration method varied with different parameters: (1) The power supplied to the adsorbent, (2) The duration for which the power was supplied, (3) Flow and composition of the purge gas used, (4) Use of a vacuum step instead of a purge. The impact of the regeneration on purity, recovery and energy usage were investigated. This was performed for different monoliths with different electrical properties.
It was demonstrated that the 3D-printed activated carbon monolith could be heated above 100°C in less than 20 s. In the figure left, homogenous heating of a 3D-printed monolith is shown. Using a biogas composition as feed, the enhancement on the CO2 concentration was important as can be seen in the figure right. Adsorption steps were performed before and after the regeneration and the impact on the capacity was minor, while the increase in concentration is important.
Captions for figures:
Figure left: Thermal images of Joule heating (5V) of a 3D-printed monolith (AC + phenolic binder). Electrodes used in this pictures was cupper sponge.
Figure right: Joule heating experiment performed at 4V with mass spectrometer (MS) and temperature signal. 0-105 s: Heating by the sides of 3D-printed monolith; no gas flow through adsorbent, which is open to MS. 105-135 s: Short purge step with N2 (100 Nml/min, 30s). Note: Temperature was measured 1 cm behind the monolith and is therefore an underestimation of the real temperature of the adsorbent.
References:
- Ribeiro, R. P. P. L., Grande, C. A., and Rodrigues, A. E. (2014). Electric swing adsorption for gas separation and purification: a review. Separation Science and Technology 49, 1985â2002.
- Keller, L., Lohaus, T., Abduly, L., Hadler, G., and Wessling, M. (2019). Electrical swing adsorption on functionalized hollow fibers. Chemical Engineering Journal 371, 107â117.
- Grande, C. A., Ribeiro, R. P. P. L., and Rodrigues, A. E. (2010). Challenges of electric swing adsorption for CO2 ChemSusChem 3, 892â898.
- Chronopoulos, T., Fernandez-Diez, Y., Maroto-Valer, M.M., Ocone, R. and Reay, D.A. (2014). CO2 desorption via microwave heating for post-combustion carbon capture. Microporous and Mesoporous Materials 197, 288-290.
- Querejeta, N., Plaza, M. G., Rubiera, F., Pevida, C., Avery, T., and Tennisson, S. R. (2017). Carbon monoliths in adsorption-based post-combustion CO2 Energy Procedia 114, 2341â2352.
- Couck, S., Cousin-Saint-Remi, J., van der Perre, S., Baron, G. v., Minas, C., Ruch, P., and Denayer, J. F. M. (2018). 3D-printed SAPO-34 monoliths for gas separation. Microporous and Mesoporous Materials 255, 185â191.
- Couck, S., Lefevere, J., Mullens, S., Protasova, L., Meynen, V., Desmet, G., Baron, G., and Denayer, J. F. M. (2017). CO2, CH4 and N2 separation with a 3DFD-printed ZSM-5 monolith. Chemical Engineering Journal 308, 719â726.