(57b) Effects of Alumina Films on N-Doped Carbon Nanotubes/Graphene Composites As Anode Materials of Lithium-Ion Batteries

A carbon nanotubes/graphene composite is grown on nickel foil without additional catalysts by one-step ambient pressure chemical vapor deposition (CVD). Next, the carbon nanotubes/graphene composite is modified by radio frequency (RF) nitrogen-plasma. Finally, to improve its initial coulombic efficiency/electrochemical stability, lower potential during the charge process (coin cell), and boost potential during the discharge process (lithium-ion battery), alumina is deposited onto the N-doped carbon nanotubes/graphene composite by RF magnetron sputtering at different power levels and periods of time. The charge specific capacity (597 mAh/g) and initial coulombic efficiency (81.44 % › 75.02 % for N-doped carbon nanotubes/graphene) of Al₂O₃/N-doped CNTs/graphene for the coin cell reached a maximum at the best sputtering condition (power = 65 W and time = 30 min). Al₂O₃/N-doped CNTs/graphene (the best sputtering condition) exhibits higher initial coulombic efficiency (79.8 %) compared with N-doped CNTs/graphene (initial coulombic efficiency: 74.3 %) for the lithium-ion battery. Furthermore, the achievement fraction (about 70 %) of full charge capacity (coin cell) for Al₂O₃/N-doped carbon nanotubes/graphene (the best sputtering condition) is higher than that (about 30 %) for N-doped carbon nanotubes/graphene at a voltage lower than about 0.25 V. Moreover, it also shows a little higher electrochemical stability (coin cell) of charge capacity for Al₂O₃/N-doped carbon nanotubes/graphene (the best sputtering condition) in comparison with N-doped carbon nanotubes/graphene and Al₂O₃/N-doped CNTs/graphene (the best sputtering condition) exhibits better cyclic stability (lithium-ion battery) of discharge capacity compared with N-doped CNTs/graphene.