(107a) Synthesis of Polystyrene-Silica Composite Particles Via One-Step Nanoparticle-Stabilized Emulsion Polymerization
AIChE Annual Meeting
2009
2009 Annual Meeting
Engineering Sciences and Fundamentals
Particle Synthesis and Stabilization
Monday, November 9, 2009 - 12:35pm to 12:55pm
Polystyrene-silica core-shell composite particles are prepared by one-step emulsion polymerization with a nonionic initiator VA-086, solely stabilized by silica nanoparticles. The silica nanoparticles are successfully incorporated as the shell, likely due to the fact that the nanoparticles are thermodynamically favorable to adsorb and remain at the liquid-liquid interfaces during the emulsion polymerization. The silica content, determined by thermogravimetric analysis, is approximately 20 wt% in the composite particles. In addition, we further explore the polymerization mechanism by studying the particle growth as a function of initiator concentration and reaction time: when the initiator/monomer ratio is increased from 0.83 wt% to 2.5 wt%, the particle size at 24 hour reaction time decreases for a fixed monomer amount, possibly due to a larger number of nuclei at the initial stage of polymerization. Further increasing the initiator/monomer ratio to 4.2 wt% does not continually decrease the particle size, which may be limited by the stabilization provided by a fixed concentration of silica nanoparticles. The surface coverage also changes with initiator concentration and reaction time although the underlying mechanism is not fully understood.
Checkout
This paper has an Extended Abstract file available; you must purchase the conference proceedings to access it.
Do you already own this?
Log In for instructions on accessing this content.
Pricing
Individuals
AIChE Pro Members | $150.00 |
AIChE Graduate Student Members | Free |
AIChE Undergraduate Student Members | Free |
AIChE Explorer Members | $225.00 |
Non-Members | $225.00 |