(192c) Multifunctional Nitrogen-Rich “Brick-and-Mortar” Carbon As High Performance Supercapacitor Electrodes and Oxygen Reduction Electrocatalysts
AIChE Annual Meeting
2013
2013 AIChE Annual Meeting
Topical Conference: Nanomaterials for Energy Applications
Nanomaterials for Energy Storage III
Monday, November 4, 2013 - 4:00pm to 4:15pm
Novel porous carbon materials with excellent electronic, chemical and structural properties and high nitrogen content are desirable for many applications. Here, we show the design and synthesis of a new multifunctional porous carbon material with unique “point to plane” architecture through a simple but effective activation-free procedure. Porous carbon derived from a new type of copolymer poly (vinylidene chloride-co-acrylonitrile) serves as the nitrogen-rich “mortar”. Reduced graphene oxide layers work as “bricks” with an aim to provide an open nanoscale scaffold and connect porous carbon, as well as modulate the ratio between mesopores and micropores. This new material has large surface area (957 m2/g), high nitrogen content (6.6 at %), excellent conductivity (up to 5.1 S/cm), and favorable hierarchical meso- and microporosity. Benefiting from these intriguing features, this material shows ultrahigh specific capacitance at 361 F/g in aqueous electrolyte, far superior to that of many carbonaceous materials reported so far. The as-assembled asymmetric supercapacitors with the designed carbon material as negative electrodes and porous cobalt oxide nanorods as positive electrodes deliver a high-energy of 50.1 Wh/kg with a cell voltage of up to 1.6 V. Further, this material shows a superb electrocatalytic activity for oxygen reduction reaction in alkaline medium comparable to that of 20 wt% platinum-carbon electrodes, with much better methanol tolerant and long-term durability. We expect that this uniquely designed nitrogen-rich porous carbon material with its simple and scalable synthesis method will have great potentials for various applications in energy storage, energy conversion and catalysis.