(486a) Importance of Reaction Mechanism Involved in Design of the Catalyst and the Reactor for Future Ammonia Synthesis

Importance of reaction mechanism involved in design of the catalyst and the reactor for future ammonia synthesis

Ken-ichi Aika, Tokyo Institute of Technology, kenaika@c01.itscom.net

The ammonia synthesis reaction is considered to involve several elementary steps [1]:

N₂ + 2＊ à 2N(a) (1)

H₂ + 2＊ à 2H(a) (2)

N(a) + H(a) à NH(a) + ＊ (3)

NH(a) + H(a) à NH₂ (a) + ＊ (4)

NH₂ (a) + H(a) à NH₃(a) + ＊ (5)

NH₃(a) à NH₃ + ＊ (6)

　Here, the symbol * indicates empty sites. For most metal catalysts, the dissociative adsorption of dinitrogen (step 1) is the rate-determining step, and all the other steps and its reverse step (from 2 to 6) are fast enough to be almost in equilibrium for each reaction step. The synthesis rate is considered to be the same as the rate for step (1), and is proportional to the dinitrogen pressure and square of the empty site concentration. For iron catalysts, the main adsorbed species are simply N atoms, and the empty site concentration is given by [＊]= 1-θ_N, where θ_N is the surface coverage of N. Under equilibrium conditions, Eqs. (2) to (6) can be combined to give the following equation:

N(a) + 1.5H₂ = NH₃ + ＊ (7)

The equilibrium constant in Eq. (7), 1/K_d, is expressed as:

1/K_d = (1-θ_N)P_NH3/θ_NP_H2^1.5 (8)

The empty site concentration, (1-θ_N), is given by:

(1-θ_N) = 1 / (1+ K_d P_NH3/ P_H2^1.5) (9)

Thus, the synthesis rate can be expressed as a function of the N₂, H₂, and NH₃ pressure, as follows:

r₁ = k₁P_N2 (1-θ_N) ² = k₁P_N2 (1+ K_d P_NH3/ P_H2^1.5)^-2 (10)

Here, k₁ is the rate constant for step (1).

For ruthenium catalysts, dissociative adsorption is the rate-determining step, as with other metals, but adsorbed hydrogen has been found to retard the synthesis reaction. When both N(a) and H(a) retard dinitrogen activation, rate equation (10) is expressed instead as follows:

r = k₁P_N2 (1+ K_d P_NH3/ P_H2^1.5 + K₂ P_H2^0.5)^-2 (11)

Here, K₂ is the equilibrium constant for hydrogen adsorption (step (2)).

Thus character of the catalyst is expressed with the values of k₁ (ability of N₂ activation), K_d (strength of N adsorption), and K₂ (strength of H adsorption). Active ammonia catalyst has high value of k₁. Generally K_d is great at iron but low at ruthenium. On the other hand K₂ is great at some ruthenium catalyst (strong hydrogen inhibition. The surface nature of ruthenium catalyst is strongly affected with the support and promoter. This is the reason why a lot of unique catalysts have been reported recently. The relation between promoter compounds and kinetic indexes shall be shown in this presentation.

These indexes are necessary for the reactor design and process operation (pressure, temperature, conversion, H/N ratio). If we can install different kind of catalysts, we can set a catalyst with great K_d at the reactor inlet part, but not at the outlet part where produced ammonia depress the rate by strong K_d. Such examples shall be shown.

Another interesting issue is whether the active synthesis catalyst can be the best decomposition catalyst or not. These problems shall be also discussed in this presentation.

Future ammonia production condition might be changed when renewable hydrogen is used. This kind of study must become important.

[1]; K. Aika, "Role of alkali promoter in ammonia synthesis over ruthenium catalysts—effect on reaction mechanism", Catal. Today, 286 (2017) 14-20.