Utilization of Carbonated Bof Slag As Partial Replacement of Aggregate in Cement Mortars
International Conference on Accelerated Carbonation for Environmental and Material Engineering ACEME
2015
2015 International Conference on Accelerated Carbonation for Environmental and Material Engineering (ACEME)
Utilization of the carbonated materials
Utilization 1
Monday, June 22, 2015 - 3:45pm to 4:00pm
After direct mineral carbonation, a material rich in carbonates and with reduced quantities of free oxides is obtained. The aim of this work was to show that such materials can be used in the construction domain. Basic Oxygen Furnace (BOF) slag from the steelmaking process has been traditionally seen as unfit for bounded applications due to its propensity to swelling, resulting from hydration of its high free lime content. Here, BOF slag was crushed to suitable particle sizes, carbonated in an aqueous solution of carbonic acid, and utilized to replace 50% of natural sand aggregate in cement mortars. The mechanical and chemical properties of these mortars were compared to mortars containing non-carbonated slags, and a standard cement mortar as a reference. Tests were conducted to determine mortar flow and soundness, and cured mortar compressive strength and leaching tendencies. The results showed a satisfactory performance from all considered aspects (comparable with the reference) of the mortar sample containing 37.5 wt% (1.5 in 4 parts solids) carbonated BOF slag of <0.5 mm particle size.